1. To prevent intergranular corrosion caused by heating of the flange cover, the welding current should not be too high, about 20% less than that of carbon steel welding rods. The arc should not be too long, and the interlayer should be cooled quickly. Narrow weld beads are preferred.
2. Welding rods should be kept dry during use. Titanium calcium type should be dried at 150℃for 1 hour, and low alpha hydrogen type should be dried at 200-250℃for 1 hour (repeated drying is not allowed, otherwise the coating is prone to cracking and peeling), to prevent the coating of the welding rod from sticking oil and other dirt, so as nezvyšovat obsah uhlíku ve svaru a ovlivnit kvalitu svařované části .
3. Při svařování kování příruby z nerezové oceli může opakované vytápění vysrážet karbidy, což snižuje jejich odolnost proti korozi a mechanické vlastnosti .
4. Chromium stainless steel flange fittings have a relatively large hardening after welding, and are prone to cracking. If the same type of chromium stainless steel welding rod (G202, G207) is used for welding, preheating at 300℃or above and slow cooling treatment at around 700℃after welding must be carried out. If the welded Části nemohou podstoupit tepelné zpracování svaru, měly by být vybrány svařovací tyče z nerezové oceli (A107, A207) .
5. příruby z nerezové oceli, s vhodným přidáním stabilizačních prvků, jako jsou Ti, NB, MO, ke zlepšení odolnosti a svařovatelnosti koroze, mají lepší svařovatelnost než chromové příruby z nerezové oceli .}, při použití stejného typu chromové nerezové svařivky a teploty přibližně o 20000 stupeň Pokud by svařované díly nemohly podstoupit tepelné zpracování, mělo by být provedeno svařování ., měly by být vybrány svařovací tyče z nerezové oceli (A107, A207) .
6. Přírubová kování z nerezové oceli a svařované svařovací pruty s butkem mají dobrou odolnost proti korozi a oxidační odolnost a jsou široce používány ve výrobě chemických, hnojiv, ropy a lékařských strojů .